At least 25% greater WLL than traditional Grade 8 products.
Proof Load tested at 2.5 times the WLL with certification for each batch manufactured. Fatigue rated to 20,000 cycles at 1.5 times the WLL.
Tempering temperature minimum 400°C.
Magnaflux crack detection is performed 100% on each batch.
When fitting G10 components are added to G8 chain, the sling is rated at G8 WLL.
Material: Quenched and Tempered Alloy Steel.Marking: According to standard, Size, grade, manufacturer ID, traceability.Temperature range: -40ºC up to +200°C (without reduction in WLL).Finish: Blue painted.Standard: EN 1677-3 Safety factor: 4:1Grade: 10
Welded Master Link designed for 1 leg chain, wire rope and webbing slings.
At least 25% greater WLL than traditional Grade 8 products.
Fatigue rated to 20,000 cycles at 1.5 times the WLL.
Proof Load tested at 2.5 times the WLL with certification for each batch manufactured.
Material: Quenched and Tempered Alloy SteelMarking: According to standard, CE-marked, Type, manufacturer ID, traceability.Temperature range: -40° up to +200°C (without reduction in WLL)Finish: Blue PaintedStandard: EN 1677-4 Safety factor: 4:1Grade: 10
At least 25% greater WLL than traditional Grade 8 products.
Testing according to DIN PAS 1061 and ASTM A952/A 952M.
Proof Load tested at 2.5 times the WLL with certification for each batch manufactured. Fatigue rated to 20,000 cycles at 1.5 times the WLL.
Tempering temperature minimum 400°C.
Designed for the assembly of chain slings where wide throat openings are necessary.
Material: Quenched and tempered alloy steel.Marking: According to standard, Size, grade, manufacturer ID, traceability.Temperature range: -40ºC up to +200°C (without reduction in WLL).Finish: Blue painted.Standard: EN 1677-1 Warning: Before using the hook, check whether hooks without safety latches are allowed to be used for the particular application.Safety factor: 4:1Grade: 10
At least 25% greater WLL than traditional Grade 8 products.
Testing according to DIN PAS 1061 and ASTM A952/A 952M.
Proof load tested at 2.5 times the WLL with certification for each batch manufactured. Fatigue rated to 20,000 cycles at 1.5 times the WLL.
Designed for the assembly of chain slings where wide throat openings are necessary
When fitting G10 components are added to G8 chain, the sling is rated at G8 WLL.
Material: Quenched and Tempered Alloy Steel.Marking: According to standard, Size, grade, manufacturer ID, traceability.Temperature range: -40ºC up to +200°C (without reduction in WLL).Standard: EN 1677-1 Warning: Before using the hook, check whether hooks without safety latches are allowed to be used for the particular application.Safety factor: 4:1Grade: 10
This swivel hoist ring rotates through 360° and pivots 180°, and simultaneously allows lifting from any direction.
Load rated parts are 100% magnaflux crack detected.
Individual forged parts and cap screw are traceable to Test Certification.
Bolt are Metric thread (ASME / ANSI B18.3.1M).
Proof tested to 2.5 times the WLL.
Fatigue rated to 1.5 times the WLL.
Quick and simple assembly, just a tapped hole is required.
Features: Built-in RFID/NFC chipMaterial: Forged alloy steel, quenched and temperedMarking: According to standard, CE-markedStandard: EN 1677-1 Safety factor: 4:1
At least 25% greater WLL than traditional Grade 8 products.
Proof Load tested at 2,5 times the WLL with certification for each batch manufactured.
Fatigue rated to 20,000 cycles at 1.5 times the WLL.
Magnaflux crack detection is performed 100% on each batch.
Material: Quenched and Tempered Alloy SteelMarking: According to standard, Size, grade, manufacturer ID, traceability.Temperature range: -40ºC up to +200°C (without reduction in WLL).Finish: Blue painted.Standard: EN 1677-2 Safety factor: 4:1Grade: 10
At least 25% greater WLL than traditional Grade 8 products.
Testing according to DIN PAS 1061 and ASTM A952/A 952M.
Proof Load tested at 2.5 times the WLL with certification for each batch manufactured. Fatigue rated to 20,000 cycles at 1.5 times the WLL.
Tempering temperature minimum 400°C.
Enables full WLL while in use, thanks to supporting wings which prevent chain link deformation.
Material: Quenched and Tempered Alloy Steel.Marking: According to standard, Size, grade, manufacturer ID, traceability.Temperature range: -40ºC up to +200°C (without reduction in WLL).Finish: Painted.Standard: EN 1677-1 Note: Not for use with Omega LinkSafety factor: 4:1Grade: 10
Safety hook to be welded on the excavator bucket.
Load rated parts are 100% magnaflux crack detected.
Individual forged parts are traceable to Test Certification.
Proof tested to 2.5 times the WLL.
Fatigue rated to 1.5 times the WLL.
All YOKE Lifting points meet or exceed all the requirements of ASME B30.26.
WLL forged onto each product for quick and easy identification.
Lugs designed to assist the welding process.
A protected spring keeps the load ring in a required position. The parts are connected in such a way that they remain captive. The spring also reduces noise caused by vibrations."
Material: Forged alloy steel, quenched and tempered.Marking: According to standard, CE-marked, Size, grade, manufacturer ID, traceability.Temperature range: -40ºC up to +200°C (without reduction in WLL).Finish: Yellow painted.Standard: EN 1677-1 Safety factor: 5:1
Welded Master Link designed for 3-4 legs Wire Rope and Chain Slings.
At least 25% greater WLL than traditional Grade 8 products. Fatigue rated to 20,000 cycles at 1.5 times the WLL.
Proof Load tested at 2.5 times the WLL with certification for each batch manufactured.
Material: Quenched and Tempered Alloy SteelMarking: According to standard, CE-marked, Type, manufacturer ID, traceability.Temperature range: -40° up to +200°C (without reduction in WLL).Finish: Blue painted.Standard: EN 1677-4 Safety factor: 4:1.Grade: 10
Welded Master Link designed for 3-4 legs Wire Rope and Chain Slings.
At least 25% greater WLL than traditional Grade 8 products. Fatigue rated to 20,000 cycles at 1.5 times the WLL.
Proof Load tested at 2.5 times the WLL with certification for each batch manufactured.
Material: Quenched and Tempered Alloy SteelMarking: According to standard, CE-marked, Type, manufacturer ID, traceability.Temperature range: -40° up to +200°C (without reduction in WLL).Finish: Blue painted.Standard: EN 1677-4 Safety factor: 4:1Grade: 10
Rotates through 360° and pivot 180°, rated at 100% at 90°angle.
Load rated parts are 100% magnaflux crack detected.
Individual forged parts and cap screw are traceable to Test Certification.
Bolt are Metric thread (ASME / ANSI B18.3.1M).
Proof tested to 2.5 times the WLL.
Fatigue rated to 1.5 times the WLL.
Quick and simple assembly, just a tapped hole is required.
Material: Manufactured from forged alloy steel, quenched and tempered.Marking: According to standard, CE-markedStandard: EN 1677-1 Safety factor: 4:1
At least 25% greater WLL than traditional Grade 8 products.
Proof Load tested at 2.5 times the WLL with certification for each batch manufactured.
Fatigue rated to 20,000 cycles at 1.5 times the WLL.
Suitable for use with both Grade 8 and Grade 10 chain.
When fitting G10 components are added to G8 chain, the sling is rated at G8 WLL.
Material: Quenched and Tempered Alloy Steel.Marking: According to standard, Type, manufacturer ID, traceability.Temperature range: -40° up to +200°C (without reduction in WLL).Finish: Blue painted.Standard: EN 1677-1 Safety factor: 4:1Grade: 10
At least 25% greater WLL than traditional Grade 8 products.
Manufactured in accordance with EN 1677-3 and ASME B30.26.
Proof Load tested at 2.5 times the WLL with certification for each batch manufactured. Fatigue rated to 20,000 cycles at 1.5 times the WLL.
Tempering temperature minimum 400°C.
Magnaflux crack detection is performed 100% on each batch.
When fitting G10 components are added to G8 chain, the sling is rated at G8 WLL.
Material: Quenched and tempered alloy steel.Marking: According to standard, Size, grade, manufacturer ID, traceability.Temperature range: -40ºC up to +200°C (without reduction in WLL).Finish: Blue painted.Standard: EN 1677-3 Safety factor: 4:1Grade: 10
Welded Master Link designed for 1-2 legs Wire Rope and Chain Slings. The engineered flat makes it simple to insert wire rope thimbles on our links. Suitable for omega links.
At least 25% greater WLL than traditional Grade 8 products.
Proof Load tested at 2.5 times the WLL with certification for each batch manufactured. Tempering temperature at a minimum of 400°C.
Material: Quenched and Tempered Alloy Steel.Marking: According to standard, CE-marked, Type, manufacturer ID, traceability.Temperature range: -40° up to +200°C (without reduction in WLL).Finish: Blue painted.Standard: EN 1677-4 Safety factor: 4:1Grade: 10
Container Hook CH-3
Material: Alloy steelMarking: According to standard, CodeTemperature range: -40ºC up to +200°C (without reduction in WLL).Finish: Yellow painted.Standard: EN 1677-1 Warning: Not for topliftSafety factor: 4:1Grade: 8
At least 25% greater WLL than traditional Grade 8 products.
Fatigue rated to 20,000 cycles at 1.5 times the WLL.
Fully integrated shortening hooks and master link.
No reduction in WLL when shortening chain.
Speedy assembly.
Light weight system.
Cost effective compared to slings which use multiple components.
Proof Load tested at 2.5 times the WLL with certification for each batch manufactured.
Material: Quenched and Tempered Alloy Steel.Marking: According to standard, CE-marked, Type, manufacturer ID, traceability.Temperature range: -40° up to +200°C (without reduction in WLL).Finish: Blue paintedStandard: EN 1677-4 Safety factor: 4:1Grade: 10
Welded Master Link designed for 3-4 legs Wire Rope and Chain Slings.
At least 25% greater WLL than traditional Grade 8 products. Fatigue rated to 20,000 cycles at 1.5 times the WLL.
Proof Load tested at 2.5 times the WLL with certification for each batch manufactured
Material: Quenched and Tempered Alloy SteelMarking: According to standard, CE-marked, Type, manufacturer ID, traceability.Temperature range: -40° up to +200°C (without reduction in WLL).Finish: Blue painted.Standard: EN 1677-4 Safety factor: 4:1Grade: 10
YOKE snatchblocks are available from 2 tons to 8 tons, for wire rope sizes 8 mm to 19 mm. Supplied with bronze bushings and 4.5”-14” with pressure lube fittings.
Fatigue rated.
Permanent batch codes link to test certificates for easy traceability.
Meets or exceeds all requirements of ASME B30.26 and have ABS type approval.
Material: Highest quality tensile steel.Marking: Part number, wire rope size and working load limit.Finish: Yellow and blue painted.Safety factor: 4:1
At least 25% greater WLL than traditional Grade 8 products.
Testing according to DIN PAS 1061 and ASTM A952/A 952M.
Proof Load tested at 2.5 times the WLL with certification for each batch.
Fatigue rated to 20,000 cycles at 1.5 times the WLL.
Enables full WLL while in use, thanks to supporting wings which prevent chain link deformation.
Extra safe pin.
Material: Quenched and Tempered Alloy Steel.Marking: According to standard, Size, grade, manufacturer ID, traceability.Temperature range: -40ºC up to +200°C (without reduction in WLL).Finish: Blue painted.Standard: EN 1677-1 Note: Not for use with Omega Link.Safety factor: 4:1Grade: 10
The eyes can be loaded with working load limit in all directions, pivots through 180°. Load rated parts are 100% magnaflux crack detected.
Individual forged parts are traceable to Test Certification.
Proof tested to 2.5 times the WLL, fatigue rated to 1.5 times the WLL.
A protected spring keeps the load ring in a required position. The parts are connected in such a way that they remain captive. The spring also reduces noise caused by vibration.
Material: Manufactured from forged alloy steel, quenched and tempered.Marking: According to standard, CE-marked, WLL, size, steel quality, manufacturer ID and traceability.Standard: EN 1677-1
Fully integrated shortening hook and master link.
At least 25% greater WLL than traditional Grade 8 products.
Fatigue rated to 20,000 cycles at 1.5 times the WLL.
No reduction in WLL when shortening chain.
Speedy assembly.
Light weight system.
Cost effective compared to slings which use multiple components.
Proof Load tested at 2.5 times the WLL with
certification for each batch manufactured.
Material: Quenched and Tempered Alloy Steel.Marking: According to standard, CE-marked, Type, manufacturer ID, traceability.Temperature range: -40° up to +200°C (without reduction in WLL).Finish: Blue paintedStandard: EN 1677-4 Safety factor: 4:1Grade: 10
Forged alloy wide body shackle with bolt pin.
All shackles with batch Code which links to Test Certificate and quality traceability.
Proof Load tested at 2.5 times the WLL with certification for each batch manufactured.
Fatigue rated to 20,000 cycle fatigue rated to 1.5 times Working Load Limit.
100% magnaflux crack detection during manufacturing.
Material: Shackles are forged alloy steel with alloy pin.Marking: CE-marked, Size, WLL, manufacturer ID, traceability.Temperature range: -40°C up to +200°C (without reduction in WLL).Finish: Blue painted.Safety factor: 5:1Grade: 10
Pivots to 230°, rotates through 360° due to its unique ball bearing design.
Certified by DGUV GS-OA-15-04.
Load rated parts are 100% magnaflux crack detected.
Individual forged parts and batch code links to Test Certificate sheet.
Bolt are Metric thread (ASME / ANSI B18.3.1M).
Proof tested to 2.5 times the WLL.
Fatigue rated to 1.5 times the WLL.
All YOKE Super points meet or exceed all the requirements of ASME B30.26.
Easy to attach or dismantle due to the forged hexagon shaped body of the Super Point.
Capable of rotating under load.
With the new WLL tables you can find the right Super Point attachment for your application and by the red marking on both sides you can measure disposal stage of the Super Point.
Features: Built-in RFID/NFC chipMaterial: Forged alloy steel, quenched and tempered.Marking: According to standard, CE-markedTemperature range: -40°C - +200°CStandard: EN 1677-1 Warning: Do not turn continuously in 90 degree direction at full load.Safety factor: 4:1